Applicability of SiC coating through CVD process and PCS(polycarbosilane) impregnation for the oxidation resistance and mechanical properties of C/C composite was studied. The SiC layer coated by CVD was deposited uniformly on the C/C composite, whereas the SiC converted from PCS impregnation wetted around individual carbon fiber. The PCS-impregnated C/C composite exhibited a significant increase of bending strength in comparison with as received C/C composite. This increase in the mechanical property could be attributed to the high bonding strength between fibers due to an impregnated SiC phase. The PCS-impregnated C/C showed 25% improvement in density, 3.5 times higher MOR and 2.8 times higher oxidation resistance compared to the as-received C/C. The increments due to PCS impregnation were more effective than CVD process.