Specific structural properties of Li intercalation reaction into the spinel relatedmanganese dioxide, $Li_{x}Mn_{2}O_{4}(0.2{leq}x{leq}2.0)$, are investigated by X-ray diffractional and electrochemical studies of Li/1M $LiClO_{4}$-propylene carbonate solution/$Li_{x}Mn_{2}O_{4}$ cell. The effect of the chemical composition and the reaction temperature on electrochemical parameter of $Li_{x}Mn_{2}O_{4}$ are studied by the phenomena of phase-transition, analysis of crystal lattice, fine structure, and thermal analysis. Treatment of the spinel $Li_{x}Mn_{2}O_{4}$ with aqueous acid was found to result in conversiton of $Li_{x}Mn_{2}O_{4}$ to nearly pure $MnO_{2}$, as evidenced by a reduction in the lattice constant $a_{c}$ from 8.255 to $8.031;{AA}$. At a composition range of $0.2{leq}x{leq}0.6$ in $Li_{x}Mn_{2}O_{4}$ the reduction proceeded in a homogeneous phase, which was characterized by a constant voltage of 3.9~3.7 V together with a lattice constant of $8.255;{AA}$.