In following addition of 0.3, -0.6, 0.8, 1.0 and 5 weight percent MgSiF66H2O studies have been made of the setting and hardening characteristics of ordinary portland cement. MgSiF66H2O retarded the setting time of ordinary portland cement and extended the induction pariod of the hydration. In ordinary portland cement the setting characteristics were drastically altered especially at high MgSiF66H2O contents. Evidence was also obtained by the formation of a KSiF6 which was very fine particle. The results wee as follows. 1. Slump was slightly decreased when MgSiF66H2O added. 2. Setting time was retarded depending on the amount of retarding agent 2 to 8 hours 3. Compressive strength was almost same or some increased in comparision with opc. 4. When MgSiF66H2O was added to cement paste K2SiF6 were formed It was fine-sized distributed uniformly in cement grain and caused retardation of cement setting.