Kalsilite (KAlSiO4) system undergoes a displacive phase transition from hexagonal phase with p63 space group to the phase with P63mc at 886$^{circ}C$. The flux composition having kalsilite :K2O:B2O3=1:2:2 has enabled the growth of hexagonal kalsilite with the size of 0.5~1 mm at a slow cooling rate (0.3$^{circ}C$/hr). On decreasing the cooling rate the size has increased and pyramidal (1011) faces are newly developed with the shape of (0001) and (1010) faces. Upon stirring (1011) faces are degraded. The space group of O1 and O2 are P21221 and C2221 respectively. Their orthorombic modification O1 and O2 are synthesized at relatively low and high temperature respectively.