Toughening mechanism of boron carbide ceramics by the addition of titanium boride was investigated. Speci-men was prepared by hot pressing of boron carbide with upto 30vol% of titanium boride particulates. Toughness of boron carbide ceramics was increased from 4.7 MPa m1/2 to 6.3 MPa m1/2 with 15 vol% TiB2 addition. But further increase of TiB2 content results in slow decrease of toughness. From microstructure evaluation and crack propagation behavior it is concluded that the major toughening mechanism is crack deflection pheno-mena.