To investigate the final structures and reactions of silicides a somewhat thick Ti monolayer Co monolayer and Co/Ti bilayer films were deposited on single Si(100) wafer by electron beam evaporation followed by heat treatment using RTA system in N2 ambient. TiO2 film formed between Ti and TiSi2 layers due to oxgen or moisture in the Ti monolayer sample. The final layer structure obtained after the silicidation heat-treatment of the Co/Ti bilayer sample turned out to be TiSi2/CoSi2/Ti-Co-Si alloy/CoSi2/Si sbustrate. This implies that imperfect layer inversion occurred due to the formation of Ti-Co-Si intermediate phase.