Green sheet was prepared by tape casting in the composition of (1-x)Pb(Mg1/3Nb2/3)O3-PbTiO3 system using Pb(Mg1/3Nb2/3)O3 and PbTiO3 synthesized with PbO, Nb2O5 MgO and TiO2 The densest green sheet was obtained in the weight ratio 70:30 of powder to binder. Green sheet wasmultilayered in metal mould and formed into lamination at 7$0^{circ}C$, 300kg/cm2 The lamination was sintered at 110$0^{circ}C$ 2hr, Dielectric constant and Curie temperature of disc type sintered body was highered with increasing the amount of PbTiO3 and was in the range of 19000-21000, -7~45$^{circ}C$ respectively. Green and sintered relative density of lamination was 61% and 95% respectively.