Polyethylene Terephthalate (PET) has been used as a mainstream fiber to make silklike fiber. The silky characteristics such as softness, dry touch feeling and flexibility can be obtained by weight reduction treatment. In aqueous alkali solution, the surface of PET is dissolved away and reduced in weight. The PET fiber, yarn and fabric become thinner and the gaps between fibers are wider. Its mobility is greatly improved without change of basic structures of the treated PET fibrics. The alkali treatment was conducted under the various experimental conditions such as alkali (NaOH) concentration, treatment time and temperature. As the weight loss increased, drapability improved and tensile strength remarkably reduced. When the PET fabrics lost 30% in their weight, drape coefficient lowered as much as 30oA and tensile stregth lowered as much as 50%. The weight loss over 30% brings great improvement in drapability and dyeability and significant decline in durability. By the alkali treatment, absorbency in spectrophotometer of dyed PET can be increased as much as 82% due to the increase of the surface area and formation of microvoids on the surface.