This study was carried out to investigate the effects of dyeing on the mechanical properties, primary hand, total hand value (THV), and total appearance value (TAV) of woven fabrics. Cotton, PET, nylon, cotton/PET, and cotton/nylon woven fabrics were used as test specimens. Each of fabric was dyed under the same conditions as the fabrics for sportswear which consumers have selected as best. Mechanical properties of specimens were measured by KES-FB system and primary hand and THV were calculated by equation KN -201-MDY and KN-301-WINTER respectively. TAV was calculated by KN (eq. 10). The results were as follows: 1. In mechanical properties. tensile energy increased when cotton and two cotton mixture fabrics were dyed and decreased when polyester and nylon fabrics were dyed. Bending rigidity and shear rigidity decreased after all fabrics were dyed except nylon and cotton/ nylon mixture fabrics showing higher rigidities. Cotton fabrics showed higher surface roughness while other fabrics did lower values after dyeing. 2. In evaluation of primary hand and total hand , four primary hands of cotton fabrics so decreased after dyeing that THV were lowered. Numeri, Fukurami, and Sofutosa in primary hand of polyester, cotton/polyester, and cotton/nylon fabrics and Koshi and Numeri of nylon fabrics increased after dyeing and therefore THV of four fabrics were improved. 3. Cotton and polyester fabrics showed higher TAV due to their lower bending and shear rigidity, while nylon and cotton/nylon fabrics did lower values due to their higher shear rigidity. 4. It was proposed that the method of dyeing or treatment for minimizing the decrease of THV of cotton fabrics and TAV of nylon fabrics should be developed.