0.15(B $a_{0.95}$ S $r_{0.05}$)O-0.15(S $m_{2(1-x}$/N $d_{2x}$) $O_{3}$-0.7Ti $O_{2}$(x=0-10[m/o]) ceramics were fabricated by mixed oxide method. Microwave dielectric properties were investigated with contents of N $d_{2}$ $O_{3}$. In the case of specimen with N $d_{2}$ $O_{3}$(6[m/o]), dielectric constant, quality factor and temperature coefficient of resonant frequency were 78.14, 2938(at 3[GHz]) and +14.19[ppm/.deg. C], respectively. By comparison its properties with undoped specimen, dielectric constant and quality factor were highly improved, but the temperature coefficient of resonant frequency was increased to positive value......