Automobile Fuel Shortage Detecting Sensor, in this paper, was fabricated by using heat dissipation coefficient difference between gasoline and air condition the NTC thermistor of Mn-Ni Co system with the composition ratio of Mn$_{3}$O$_{4}$ : 9wt%, NiO : 28wt%, and CO$_{3}$O$_{4}$ : 61wt%. The condition of sensor operation is that, for turn-on characteristics, the time of arriving at 135mA must be less than 180 second when the DC voltage of 11V is applied in the air condition of -10.deg. C and that, for turn-off characteristics, the saturation current must be less than 60mA when the DC voltage of 15V is applied in the gasoline condition of 60.deg. C. It is known, from the experimental results, that the resistance range and B-constant for the Automobile Fuel Shortage Detecting Sensor with dimension of 5*3*0.9mm were 850-1150.ohm. and 1150-1250.deg. C, respectively and the resistance range and B-constant were agree with that of sensor operation condition. When Bi$_{2}$O$_{3}$ of 0-0.5wt% was added to Mn$_{3}$O$_{4}$ : 9wt%, NiO : 28wt%, and CO$_{3}$O$_{4}$ : 61wt% composition, the resistivity and B-value were 380-430(.ohm.-cm) and 1930 - 2030, respectively. Particularly, for Bi$_{3}$O$_{3}$ of 0.25-0.5wt%, the sintering density of over 90% and the operation characteristics necessary to Automobile Fuel Shortage Detecting Sensor were obtained. The difference of heat dissipation coefficient gasoline and air condition was 15 times.