The applications of the high density plasma sources to the etching in semiconductor fabrication process are actively studied because of the more strict requirement from the dry etching process due to shrinking down of the critical dimension. But in the oxide etching with the high density plasma sources, abundant fluorine atoms released from the flurocarbon feed gas make it difficult to get the highly selective $SiO_2/Si$ etching. In this study, to improve the $SiO_2/Si$ etch selectivity through the control of the radical loss channels, we propose the wall heating , one of methods of controlling loss mechanisms. With appearance mass spectroscopy(AMS) and actinometric optical emission spectroscopy(OES), the increase of both radicals impinging on the substrate and existing in bulk plasma, and the decrease of the fluorine atom with wall temperature are observed. As a result, a 40% improvement of the selectivity was achieved for the carbon rich feed gas.