Neutral Zinc Electroplating(NZE) utilizing the electrolyte of pH 6 to 8 has advantages in waste treatment and the protection of equipment. NZE is beneficially used in chromating treatment, but the limiting current density and the current efficiency are low. Therefore this study is investigated to analyse the characteristics of NZE and to obtain high current density and current efficiency. The deposition potential of zinc in the NZE bath is about 110mV, which is lower than acidic bath. The current density possibily increases up to 60A/d$m^2$ in lower complexing agent content and pH 6. More than 90% of cathodic current efficiency was obtained in NZE bath. The NZE morphology shows smaller grains than acidic bath. The addition of 4$mell$/1 second brightener gives finer morphology. As pH becomes higher, (002) plan decreases and (100), (101) and (110) planes increase in the no additives solution.