In order to Improve the fracture toughness of epoxy resin system, liquid chloroprene rubber(LCR) and liquid butadiene rubber (LBR) which have hydroxy group were used in the brittle epoxy system. Mechanical and toughness characterization of the modified epoxy resins were investigated as a function of liquid rubbers content. Epoxy resins modified with both of the liquid rubbers showed complete phase-separation microstructure : In all of the LCR content, it was observed that the domain size of LCR dispersed in the epoxy matrix ranging from $2{mu}m;to;5{mu}m$. It was found that fracture toughness, $K_{ic}$, of the modified LCR system was enhanced continuously as increasing LCR content. However around 10phr of LBR system showed maximum fracture toughness. Specifically, when BPA add to the modified LCR system, thermal and mechanical properties increased than neat epoxy. At the same time, fracture toughness was enhanced.