Electochromic tungsten oxide thin films were prepared on the ITO coated glass by rf magnetron sputtering from a compressed powder tungsten oxide target in an argonoxygen atmosphere. The influence of the preparation conditions, especially the substrate temperature, on the chemical stability of film was investigated. These films were cycled in 0.6M $LiClO_4$ and 0.6M $H_2SO_4$ electrolyte respecitively, and exhibited electrochromic behavior upon the electrochemical insertion and extraction of ion. Among these tungsten oxide thin films, films prepared at a substrate temperature of $150^{circ}C$ were found to be most stable in terms of cyclic durability.