The arc stability and the metal transfer mode of high deposition GMA welding were investigated using various compositions of shielding gas with two types of filler, ie solid wire and metal cored wire. As for a solid wire, the transfer mode changed from axial spray to rotational spray with increasing wire feed rate (welding current) and the transition current was different with the gas composition. The gas composition also affected the apparent stability of rotating arc. As for a metal cored wire, on the other hand, no transition occurred and thus spray transfer mode could be applied with the welding current over 500A (deposition rate over 300g/min). Looking for the development of high deposition GMA welding process, above results were discussed in two different ways, one is to elevate the transition current, the other is to stabilize the rotational transfer mode.