In this study, the amorphous foil filler, thickness of 20 - $20~30mu extrm{m}$ was made to develop Cu-7.5wt%Mn-7.5wt%Si insert alloy(melting point temperature : solidus line 1003K, liquidus line 1070K). Liquid phase diffusion bonding of 304 stainless steels (STS304), is carried out successfully by using developed Cu-7.5Mn-7.5Si insert alloy. Bonding conditions are taken from bonding pressure of 5MPa, bonding temperatures from 1073K to 1423K varied within 50K and brazing holding times of 0, 30, 60 and 240 minutes. As the results, the tensile strength in the liquid phase diffusion bonding is a little bit lower than that in the solid phase diffusion bonding. The authors find out that the liquid phase diffusion bonding needs lower bonding pressure than the others. Therefore, the liquid phase diffusion bonding had an excellent brazability in which the bonding process showed the typical mechanism of diffusion bonding. In corresponding, the new developed insert alloy of low melting pointed Cu-7.5Mn-7.5Si makes possible brazing between the STS304.