The synthesis of high purity and ultra-fine $BaTiO_{3}$ by precipitation with gaseous $NH_{3}$ as precipitator was investigated to find an alternative process to solve various problems of present wet methods. This study consisted of two parts ; synthesis of $BaTiO_{3}$ precipitation with gaseous $NH_{3}$ and test of electrical property for the $La_{2}O_{3}$ doped $BaTiO_{3}$. The proper condition for the synthesis of $BaTiO_{3}$ by precipitation with gaseous $NH_{3}$ is as follows. The pH was 9.0. $H_{2}O_{2}$ mole ratio to $TiCl_{4}$ was 10. $NH_{3}$ gas follow rate did not influence the synthesis of $BaTiO_{3}$. The calcination temperature of $BaTiO_{3}$ was $300^{circ}C$. Also, the synthesis of $La_{2}O_{3}$-doped $BaTiO_{3}$ was tested through the wet process. Under these condition, the shape of prepared $BaTiO_{3}$ powder was spherical type and the size of that was about $0.2{mu}m$. After the powder was pressed, this green body was sintered at the $1300^{circ}C$. Under these conditions, the water absorptance and the density of the obtained sintered body were below 0.04 %, 5.2 g/$cm^{3}$, respectively. Also the grain size of that was about $10{mu}m$ and it was similar to commercial product.