Anti-reflective and anti-static double layered films were prepared on the VDT panel by sol-gel spin-coating method. Their electrical, opticla, and mechanical properties were investigated. The outer SiO2 film with low re-fractive index was coated over the inner ATO(Antimony-doped Tin Oxide)-SiO2 film which was prepared by mixing ATO sol with SiO2 at molar ratio of 68:32 to satisfy the interference condition of double layers. The heat treatment was conducted at 45$0^{circ}C$ for 30 min where residual organics were completely removed. The sheet resistance of ATO single layer showed the minimum value of 6$ imes$107$Omega$/$square$ at 3 mol% addition of Sb and that of SiO2/ATO-SiO2 increased slightly with increasing SiO2 mol% up to 30 mol%, and then increased steeply to the value of 3$ imes$108$Omega$/$square$ at 32 mol%. The reflectance of double layered films was about 0.64% at the wavelength of 550nm and the transmittance increased about 3.20%. The hardness of double layered films was almost the same as that of uncoated VDT panel, 471.4kg.f/mm2.