The powder preparation by using emulsion drying method, one of the chemical powder fabrication methods has the advantages; easy to control the chemical stoichiometry and to fabricate homogeneously fine particles. In the present study, the initial morphology and size distribution of the powder fabricated by using emulsion dry-ing method were controlled and were improved the homogeneity. By carefully controlling the mixing ratio of oil phase and aqueous solution and surfactant of preventing emulsion separation, the Bi(Pb)-Sr-Ca-Cu-O su-perconducting powders were prepared. The properties of the superconducting powder fabricated by this method and the microstructures and superconducting properties of the pelletized samples were investigated. The microstructures and electric properties of the tapes prepared by oxide powder-in-tube method were in-vestigated. The fabricated powder was spherical with less than 1$mu$m but most of them was agglomerated with 2~5$mu$m in size. The critical temperature of the pelletized sample annealed at 84$0^{circ}C$ for 72 hours in oxygen par-tial pressure of 1/13atm in Ar atmosphere was 108K. And the critical current of the first and second annealed tapes in air prepared by oxide powder-in-tube process were 0.4A and 1.5A, respectively.