The aim of this study was to investigate the degradation of piezoelectric properties with compressive cy-clic loading, the change in bending strength before and after poling treatment and fracture strength in MPB depending on the amount of MnO2 addition. The MPB with 0.25 wt.% MnO2 showed the best resistance against the piezoelectric degradation with compressive cyclic loading. Bending strength increased when pol-ing and loading directions are parallel, however decreased when poling and loading directions are per-pendicular each other. Because, during poling treatment, compressive residual stress is generated in the pol-ing direction but tensile residual stress in the perpendicular direction to poling direction.