The 2, 4, 6 and 8mol% Y2O3 doped-ZrO2 powders (20 kinds) with the addedtion of Al2O3 upto 8wt% were prepared by coprecipitation method using the zirconium oxyacetate, yttrium chloride and aluminum nitrate as starting materials. The coprecipitated powders were characterized by XRD, TG-DTA, FT-IR and SEM. The sintering properties of zirconia-alumina composites prepared by 2YSZ and 8YSZ powders containing various Al2O3 contents were also investigated. With increasing the yttria stabilizer contents, the amount of exothermic heat for zirconia crystallization decreased. And it was confirmed that the crystallizing temperature of coprecipitated zirconia powders increased and the crystallization process occurred in a wide temperature range, as Al2O3 content increased in 8YSZ.