The purpose of the study was to investigate the shrinkage and creep behavior of PET filaments which were prepared at various spinning speeds(3,300, 4,000, 5,000, 6,000, and 7,000m/min) and anneal($120^{circ}$, 30min & $150^{circ}$, 40min). In order to determine the shrinkage and creep behavior with the crystallinity change, PET filaments were treated with low(12$0^{circ}C$, 30min) and high($150^{circ}$, 40min) temperature conditions with hot air dryer under the constant tension. The results of the study were as follows: as the spinning speed increased, the degree of shrinkage and elongation of the sample treated by wet condition decreased. The sample with 0.01g/d of load under various spinning speeds showed shrinkage behavior and highest shrinkage ratio at $76^{circ}$ which was Tg of PET. The degree of shrinkage and elongation of the treated sample was less than those of the untreated sample by wet treatment. Especially, there was less degree of shrinkage and elongation of the sample treated by higher temperature condition. In 3,300m/min of spinning speed the draw ratio of undrawn yarn of a mixture of a-axis orientation and c-axis orientation was 2.0, which is similar to the value of the traditional drawn yarn. Finally, there was a big range of shrinkage and elongation by wet treatment in 3,300 m/min of spinning speed.