The photomachinable glass-ceramics of Ag and CeO$_{2}$ added to Li$_{2}$O-Al$_{2}$O$_{3}$-SiO$_{2}$-K$_{2}$O glass system was investigated as a function of UV irradiation time. The temperature of optimum nucleation and crystal growth temperature were confirmed at 525.deg. C, 630.deg. C respectively using DTA and TMA. The phases of Li$_{2}$O.SiO$_{2}$ habit were lath-like and/or dendrite type and [002] direction of Li$_{2}$O.SiO$_{2}$ / Li$_{2}$O.2SiO$_{2}$ phases were changed according to the UV irradiation time by 400 W, 362 nm UV light source. Under that condition, the optimum UV irradiation time was 5 min.