This paper evaluated the feasibility of laser consolidation for improving the properties of the plasma coated layer, Further, the mechanim of the degradation sequence of the chrome carbide layer applied on the turbine blades was postualted. The laser consolidation could be successfully applied for improcing the surface properties of the plasma coated blade, if a proper condition was carefully chosen. The consolidated layer had erosion & corrosion resistance and vond strength superiro to those of the as-plasma coated layer. The properties of the consolidated layer were strongly dependent upon the degree of dilution, especially on the Fe pickup from the substrate. The degradation of the plasma coating layer was thought to be a reault of the repeating action of the solid particle erosion, corrosion penetration through the pores and oxide films formed along the interlayer surface and impact spalling.