Die sinking electrical discharge machining(EDM) was conducted for ceramic composite of 33 weight percent TiC based on AI$_{2}$O$_{3}$ ceramic matrix according to the change of current and duty factor(DF). Material removal rate(MRR) was increased as the current and the duty factor increased, but better surface mor-pholoty was obtained in the region of lower current and duty factor. From the scanning electron microscopy(SEM) photographs and the energy dispersive X-ray spectroscopy(EDX) of the EDMed surface, EDM trace formed by one discharge spark was analyzed. Although the bending strength after EDM was highly decreased, reliability obtained by weibull analysis was increased twice. The bending strength was recovered or more by barrel polishing after EDM. From the FEM analysis of temperature for one spark, the possible melting region of AI$_{2}$O$_{3}$and TiC was obtained.