The reaction mechanisms of dry cleaning with UV-excited chlorine radical for Zn, Fe and Ti trace contaminants on the Si wafer have been studied by SEM, AFM and XPS analyses in this work. The patterned Zn, Fe and Ti films were deposited on the Si wafer surface by thermal evaporation and changes in the surface morphology after dry cleaning with $Cl_2$and UV/$Cl_2$at $200^{circ}C$ were studied by optical microscopy and SEM. In addition, changes in the surface roughness of Si wafer with the cleaning was observed by AFM. The chemical bonding states of the Zn, Fe and Ti deposited silicon surface were observed with in-line XPS analysis. Zn and Fe were easily cleaned in the form of volatile zinc-chloride and iron-chloride as verified by the surface morphology changes. Ti which forms involatile oxides was not easily removed at room temperature but was slightly removed by UV/$Cl_2$at elevated temperature of $200^{circ}C$. It was also found that the surface roughness of the Si wafer increased after $Cl_2$and UV/$Cl_2$cleaning. Therefore, the metallic contaminants on the Si wafer can be easily removed at lower temperature without surface damage by a continuous process using wet cleaning followed by UV/$Cl_2$dry cleaning.