Surface passivation using glass powders results in good reliability for high voltage silicon power devices. In this paper Zinc borosilicate glass and Lead borosilicate glass were prepared for the purpose of passivating, and a deposition technique of glass films on the silicon surface by electrophoresis in which acetone is used as a suspension medium has been investigated. Their physical properties were compared using DTA, SEM, XRD, as a function of firing temperature, I can get the fine films of 22${mu}{ extrm}{m}$ thickness with Lead borosilicate glass under 300 volts applied, 3 minutes and $700^{circ}C$ firing temperature. Also I can get the fine films of 17${mu}{ extrm}{m}$ thickness with Zinc borosilicate glass under same conditions. As a result of investigation of glass films from which glass layer was removed by placing it in HCl, it has been found that pre-firing and annealing play an important role to achieve uniform and fine glass deposition films. And also it was found that relative dielectric constant is independence of frequency.