Ternary compound ceramics, (1-y-x) BaTiO$_3$-y SrTiO$_3$-x MgTiO$_3$(0.00 x 0.20), were fabricated by the conventional ceramic process. The structural and dielectric properties of specimens were investigated while varying the composition and sintering temperature(1,200~1,45$0^{circ}C$) in order to obtain the optimum condition of capacitor. As is well known, Curie temperature(T$_{c}$) of high dielectric-based ceramic(BaTiO$_3$) was shifted and temperature of capacitance was decreased in according to increase of solid solution with (Sr, Mg)TiO$_3$. As a result, a suitable condition of compound rate for capacitor was obtained such as the BSM-11(0.8BaTiO$_3$-0.1SrTiO$_3$-0.1MgTiO$_3$), and sintering temperature was sintered at 1,25$0^{circ}C$ for two hours. In this case, dielectric constant<1,300, dielectric loss(tan$delta$)<0.03, and the variation rate of capacitance had less than 3% in the range -10~7$0^{circ}C$.>.