This study was aimed to decrease AOX(Adsorbed Organic Halide Compounds) by applying bleaching methods of A(HNO$_3$ ＋ NaNO$_2$) and $D^{(H/L)}$(dual pH chlorine dioxide bleaching) to conventional OCEDED bleaching stages. And so we investigate the effects of NSA treatment and the influence of production rate of ion species in chlorine dioxide and pulp mixtures according to various pH as well as dual pH on pulp bleaching. Finally the effects of AOC_DED^{(H/L)}ED^{(H/L)}$ bleaching stage were investigated by measuring AOX, brightness, kappa number and viscosity of pulps. A stage was treated by using 4% $HNO_3$ and 0.05~2.0% $NaNO_2$ on pulp and $D^{(H/L)}$ stage was like that pulp mixed with chlorine dioxide solution was adjusted at pH 7.0 and reacted in pulp cosistency 3%, S~20min, $70^{circ}C$, and then successively for 160~175min at pH 4.0. It was found that suitable $NaNO_2$ addition rate was at 0.6% where the brigtness of pulp was most higher and pulp viscosity was not decreased much. Chlorate ($CIO_3$) was decreased according to pH increase but chlorite($CIO_2$) was highly decreased according to pH increase. And chloride was slightly increased with pH increase. The applying of A and D^{(H/L)}$ bleaching stages to some various multiple bleaching stages ($AOC_DED^{(H/L)}/EopD^{(H/L)} etc.$) had good results that brightness was increased more 2~3% ISO than conventional method(OCEDEopD), but viscosity was dropped by only 1~2cps.