The anisotropic etching behavior of single crystal silicon were studied in aqueous KOH solution. N-type (100) oriented single crystal silicon wafers were used for the study, and the $SiO_2$ layer, whose etching rate is known to be much slower than that of silicon in the KOH solution, was used as a mask for the silicon etching. The silicon etching rate and the etching properties are shown to be a function of etchant temperature uniformity, circulation speed, and circulation direction of the etchant as well as the etchant concentration and the temperature. The etching rate is increased as the temperature is increased from $10mu extrm{m}/hr$ to $250mu extrm{m}/hr$ in the range of $50^{circ}C~105^{circ}C$. Hillock density and height is observed to be correlated with the etchant concentration and the etch temperature. The variation of the hillock density was explained by the ratio between the etching rate of (100) orientation and that of (111) orientation.