Poly-$Si_{1-x}Ge_x$ films on oxidized Si wafer were prepared by rapid thermal chemical vapor deposition using the $SiH_4$ and $GeH_4$ gaseous mixture at various deposition conditions. The deposition temperature, $SiH_4;: GeH_4$ flow ratio and pressure were varied from 400 to $600^{circ}C$, 1 : 0.1-2 : 1 and 1 to 50 torr, respectively. In this work, we have investigated the change of Ge composition of poly-$Si_{1-x}Ge_x$ films deposited with the variation of deposition parameters and the effect of Ge composition on the deposition rate. From the experimental results, it was observed that the deposition rate increased with increasing deposition temperature and Ge composition. On the other hand, the Ge composition decreased with increasing temperature. As the deposition pressure increased, the deposition rate and Ge composition were increased linearly to 10 torr but increased slowly above it, which has been attributed to the slower rate of surface reaction than mass transfer.