$Al_2O_3$/Al composite was produced by the infiltration of molten Al Into $Al_2$O$_3$ preform at 900-$1200^{circ}C$, The process was accelerated by spreading borosilicate glass powder onto the interface between Al powder compact and $Al_2O_3$ preform. Melt infiltration initialed after incubation period, and the growth of infiltration was observed to be linearly propotional with time. The major components of the composite are $Al_2O_3$ and Al with a trace of Si which is remained from borosilicate, the reaction accelerator. Relative density of the composite increased with the particle size of $Al_2O_3$ but decreased with infiltration temperature. As infiltration temperature increases from room to $950^{circ}C$ higher strength and fracture toughness were obtained.