New type of ordering along 1110] direction was found In BZT sintered at $1400^{circ}C$ for 90 hours by using X-ray diffraction analysis and high resolution transmission electron microscopy. The wavelength of the modulated structure was 0.9 nm which is three times larger than the interplanar distance of (110) plane. New type of ordering is considered to be formed as a result of Zn vancacy ordering and new structural model was proposed. The computer simulated electron diffraction and the structural images are in good agreement with those obtained by experiments.