[ $CuInTe_2$ ] synthesised in a horizontal electric furnace was found to be polycrystalline. Single crystals of $CuInTe_2$ were grown with the vertical Bridgman technique. The photoconductivity and photoluminescence of the crystals were measured in the temperature range 20 to 293 K. From the photocurrent peaks measured for the samples both perpendicular and parallel to c-axis, the energy band gaps of the samples were found to be 0.948 eV and 0.952 eV at room temperature respectively. The energy difference of the photocurrent and photoluminescence peaks of the samples both perpendicular and parallel to the c-axis measured at room temperature was a phonon energy, and its values were 22.12 meV and 21.4 meV respectively. The splitting of the valence band due to spin-orbit and crystal field interaction was calculated from the photocurrent spectra of the samples, The ${Delta}cr;and;{Delta}so$ are 0.046,0.014 eV respectively.