The purpose of this study was to compare the apical leakage and adaptation to the dentinal wall of a glass ionomer root canal cement(Ketac-Endo) with those of AH-26 and Tubli-Seal. 102 single-rooted teeth were insrumented with step-back technique and randomly divided into four groups according to kinds of root canal cements: Ketac-Endo, AH-26, Tubli-Seal, and no root canal cement. Four experimental groups were as follows; Group 1 : Filling with gutta-percha and Ketac-Endo Group 2 : Filling with gutta-percha and AH-26 Group 3 : Filling with gutta-percha and Tubli-Seal Group 4 : Filling with gutta-percha without root canal cement All the specimens were obturated with lateral condensation technique, and stored in 100% humidity for 4 days. 20 teeth in each group were placed in centrifuge tube filled with India ink, and then centrifuged for 20 minutes at 3,000 rpm. And they were evaluated for linear dye leakage using a stereoscope and analyzed by one-way ANOVA. 22 teeth were split longitudinally and evaluated the adaptation to the dentinal wall using scanning electron microscope(4 teeth in each group) and stereoscope(2 teeth in 1, 2, 3 group). The obtained results were as follows ; 1. In case of not used root canal cement(Group 4), there was showed much degree of dye penetration comparerd with used root canal cements (Group 1, 2, 3)(P<0.01). 2. In the case of used root canal cements(Group 1, 2, 3), there was no significant difference in linear leakage in groups(P>0.01). 3. In the case of used root canal cements(Group 1, 2, 3), there was showed intimate adaptation to the dentinal wall independent on kinds of root canal cements. 4. Fractured surfaces indicated failure of cohesion in Ketac-Endo, and failure of adhesion to dentine in AH-26 and Tubli-Seal. 5. According to similar apical leakage and adaptability to the dentinal wall to another root canal cements, it is possible to be used glass-ionomer cement as root canal cement.