The inhibition rate of bacteria growth per molecular weight was higher according as the molecular weight increased, the rate was the highest at the molecular weight 200,000. Microcapsule of ionized calcium was able to be produced by molecular weight 15,000, 30,000, 50,000 and 200,000 of chitosan which was dried for 48 hours after melting it in 2% of acetic acid, adding ionized calcium and controlling pH 1.2. The size of ionized calcium microcapsule was between 200 and $300;{mu}m$, the solvency, concentration and the content showed big difference by the molecular weight of chitosan. The inhibition rate of bacteria growth of microcapsule designated high in Gram positive, which was high in S. aureus, S. epidermidis and Bacillus subtilis, low in S. mutans, high in C. albicans in fungi, low in A. niger. The inhibition rate of bacteria growth of chitosan was comparatively high in Gram positive, low in S. mutans and it showed high numerical value in C. albicans of fungi. The rate recorded good result at molecular weight 200,000 relatively, there was no difference according to the molecular weight. The inhibition rate of bacteria growth according to the concentration of the microcapsule increased differently between $1.000{sim}10,000;{mu}g/ml$, it showed antibacterial activity close to the inhibition rate of growth of chitosan rather than ionized calcium. The minimum inhibitory concentration marked the highest in the mixture of chitosan and ionized calcium for all kind of bacteria generally, there was a little difference between yeast and fungi.