This study deals with the friction weldability of machine structural carbon steel (SM45C) to Al-Mg-Si aluminium alloy (A6063). The bonding strength of friction welded joints, from all mechanical test, exceeded that of A6063 base metal, under the condition of friction time 1.5 sec, upset pressure 80MPa. The friction welded joints under these conditions exhibited tensile strength of 262MPa, bending angle of 90$^{circ}$ without crack at weld interface and shear strength of 113MPa. Consequently, the friction weldability of SM4C to A6063 was very excellent, and that was possible without special preparation of weld surfaces.