In this work was produced and analyzed a z-cut Ti:LiNbO$_{3}$ optical waveguide which applies for various optical devices.A waveguide channel with a thickness 8 .mu.m and a length 66,000.mu.m and a mach-zehnder interferometer type waveguide were fabricated at a diffusion temperature 1050.deg. C for 6-8hours in a wet $O_{2}$ environment. The resulting Ti:LiNbO$_{3}$ optical waveguide was measured to have a Ti-strip thickness of 950.angs. and low loss. Surfaces and cross-sections of a fabricated waveguide were analysed. The mode pattern anaysis revealed that the waveguide showed a single mode at a 1550nm wavelength. The effective dimension of the waveguide was calculated by measuring a gaussian profile; Wx=10.95.mu. and Wy=9.14.mu.m. a propagation loss, of 0.50dB/cm for a TM mode and 0.45dB/cm for a TE mode, was low enough to be accepatable for optical devices.