Synthesis of PLT($Pb_{1-X}La_{2X/3}TiO_3$, x=0.1~0.3) powders was carried out by hydrothermal method. Optimal conditions for synthesis were $250^{circ}C$ of reaction temperature, 8M-KOH solution of hydrothermal solvent and 12 hrs reaction time, and the monolithic $Pb_{1-X}La_{2X/3}TiO_3$ particles were obtained with the composition of x$leq$0.2. The tetragonality(c/a) and the phase transition temperature were decreased by the increment of the $La_2O_3$ contents in PLT solid solutions, and the Curie temperature of the $Pb_{1-X}La_{2X/3}TiO_3$(x=0.2) was $400^{circ}C$. The shape of the synthesized particles were nearly spherical and the size was in the 20~200 nm range.