The single crystal of the $LiTaO_3$has large electro-optic effects, so it is applied to optical switch, acousto-optic deflector, and optical memory device as hologram using photorefractive effect. In this study, optic-grade undoped $LiTaO_3$and Fe:LiTaO$LiTaO_3$single crystals were grown by the Czochralski method and optical transmission and absorption spectrums were measured in the wavelength of UV-VIS range. The curie temperature was determined with DSC and by measuring capacitance for the grown undoped crystal and ceramic powder samples of various Li/Ta ratio. In case of having a 48.6 mol% $Li_2O$ as a starting Li/Ta ratio, the results of concentration variations were below 0.01 mol% $Li_2O$ all over the crystal, so it was confirmed that $LiTaO_3$single crystals were grown under congruent melting composition having optical homogeneity. The curie temperature of the Fe:$LiTaO_3$crystal was increased with increased with increased doped Fe concentrations;by the ratio of $7.5^{circ}C$ increase per Fe 0.1 wt%. Also, the optical transmittance was about 78 %, which was sufficient for optical device.