Diamond film was deposited on Mo substrate at atmospheric pressure using combustion flame apparatus with the addition of H2. At a temperature above 100$0^{circ}C$, parts of the film were converted into graphites and these were etched by hydrogen atoms. With increasing $C_2H_2/O_2$ ratio, the nucleation density of the film increased. But the greater part of the film was formed with cauliflower-shaped amorphous carbon. These amorphous carbn were crystallized etching amorphous carbon.