Alumina($Al_2O_3$)-Titanium Diboride($TiB_2) particulate composites were fabricated by hot pressing of the powder mixture that was prepared from Self-propagating High Temperature Synthesis (SHS) product and commercial powders. Their propeties were examined in order to find feasibility of using SHS for making the high performance ceramic composite. $TiB_2 particles obtained by grinding the SHS product were finer than the commercial powders. Hot pressed sample containing the SHS products exhibited higher strength than the one prepared from the commercial powders.