${eta}$-silicon carbides with yttrium aluminum garnet of 2,5,10 mol% were prepared by a liquid--phase sint-ering and the microstructural evolution and phase transformation were investigated during sintering as functions of liquid-phase amount and sintering time. The rate of grain growth decreases with the addition of the amount of yttrium aluminum garnet (YAG) in the SiC starting powder however the apparent density and the aspect ratio of grains in sintered body increase. The phase transformation from ${eta}$-SiC to ${alpha}$-SiC were dependent on the liquid-phase amount and sintering time.