Ferroelectric anomaly in PbO-{{{{ { {B }_{2 }O }_{3 } }}-{{{{ {TiO }_{3 } }}-BaO glasses which is observed in DAT measurements was in-vestigated together with the effect of BaO content on the shift of Cuire temperature. The temperature where the ferroelectric anomaly apperars on cooling in DTA decreased in proportion with increasing BaO content,. For as-crystallized samples the ferroelectric anomaly was not observed on heating but on cooling whilist for powder samples leached chemically from the crystallized samples both endothermic and ex-otehrmic peaks were observed. This fact suggests that the appearance of the ferroelectric anomaly in DAT largely depends on glassy phases surrounding individual {{{{ {PbTiO }_{3 } }} crystals rather than effects of grain size and crystallinity.