lanthanum chromite(LaCrO3) powder was synthesized by the combustion of a solution of metal nitrates La(NO3).6H2O and Cr(NO3)3.9H2O and urea. The pH of solution affected a yield of the combustion products but did not influence the morphology of the products. When the pH of the solution was in the range of 0.7-4, the yield of the combustion products was more than 90% The morphology of the combustion products was af-fected by heating methods for the solution. The hot-plate induced heating of the solution yielded powders hav-ing two-dimensionally interconnected agglomerates whereas microwave-induced heating produced a fine and non-agglomerated powders. The specific surface area(BET) of the combustion products using microwave-in-non-agglomerated powders. The specific surface area(BET) of the combustion products using microwave-in-duced heating method were larger(25~32m2) than that of hot plate heating method(10-14m2/g)/