We could obtan c-axis oriented $SrBi_2$$Ta_2$$O_9$ thin films on usual Pt(111)/Ti/$SiO_2$/Si(100) substrate using a r. f. magnetron sputtering technique. According to the increase of sputtering pressure from 250 to 300 mTorr the Bi content and degree of the c-a xis preferred orientation of $SrBi_2$$Ta_2$$O_9$ thin films were increased. By controlling Bi(or $Bi_2O_3$) loss from $SrBi_2$$Ta_2$$O_9$ thin films during post annealing and by inserting $Bi_2O_3$ layer in $SrBi_2$$Ta_2$$O_9$ thin films the effect of Bi content on the c-axis oriented growth of $SrBi_2$$Ta_2$$O_9$ thin films could be investigated without the effect of sputtering pressure. The degree of the c-axis preferred orientation of $SrBi_2$$Ta_2$$O_9$ thin films was increased with increasing with increasing Bi content by control of Bi(or $Bi_2O_3$) loss of $SrBi_2$$Ta_2$$O_9$ thin films. But the c-axis oriented growth of $SrBi_2$$Ta_2$$O_9$ thin films disappeared by the inserting of $Bi_2O_3$ lay-er in $SrBi_2$$Ta_2$$O_9$ thin films.