Effects of particle size of alumina on densification behavior during liquid-phase sintering of alumina-talc system were investigated with emphasis on particle rearrangement process. In the case of using coarse alu-mina powder densiication of specimens was rapidly accelerated after formation of liquid phase due to easy particle rearrangement process with addition of talc and increase of sintering temperature. On the contrary when fine alumina powder was used premature densification of alumina matrix region formed before for-mation of liquid phase rigid skeleton structure and then it seemed to inhibit rearrangement process during crease of sintering temperature. As results the densification of specimens using coarse alumina powder was higher than that of the case of using fine one.