$Ni_{0.65}Zn_{0.35}Cu_{0.1}Fe{1.9}O_4$ has been studied with Mossbauer spectroscopy and X-ray diffraction. The crystal structure is found to be a cubic spinel with the lattice constant $a_0=8.390{AA}$. Mossbauer spectra of $Ni_{0.65}Zn_{0.35}Cu_{0.1}Fe{1.9}O_4$ has been taken at various temperatures ranging from 12 K to 705 K. The isomer shift indicates that iron ions are ferric at tetrahedral [A] and octahedral sites [B], respectively. The Neel temperature is determined to be $T_N=705;K$. As the temperature increases toward $T_N$ a systematic line broadening effect in the Mossbauer spectrum is observed and interpreted to originate from different temperature dependencies of the magnetic hyperfine fields at various iron sites. The quadrupole splitting just on $T_N$ is 0.41 mm/s whereas the quadrupole shift below $T_N$ vanishes. This implies that the orientation of the magnetic hyperfine field with respect to be principal axes of the electric field gradient is random.