This study was carried out to understand the properties of the E.A.F. steel-making dusts for stabilization processing. The properties are related to mincral composition, shape, particle size, magnetism, density, porosity and leaching characteristic. the dust particles, the size of which ranges from sub-micron to tens-micron, were mainly spherical like balls that were agglomerated each other: the large particles were generally Fe-rich and the small particles were spherical like balls that were agglomerated each other: the large particles were franklinite (ZnFe$_{2}O_{4}$), magnetite (Fe$_{3}O_{4}$) and zincite (ZnO) by XRD analysis. When the dusts were sieved by a wet process, the particle fraction over 200 mesh had 1.5 wt.% with magnetite and quartz. The particles in the size range of 200-500 mesh consisted of magnetite, franklinite. The 82 wt.% of the steel-making dusts were occupied by the particles finer than 500 mesh and contained franklinite and zincite as main mineralogical compositions. When the dusts of around 78% porosity compressed under the load of approximately 1 KPa, the porosity decreased to 68% and to 535 under around 13 KPa. When the E.A.F. dusts were leached according to the Korea standard leaching procedure on the waster, the heavy metals exceeding the leaching criteria were cadmium, lead and mercury.